Edge illuminated photodiodes

ABSTRACT

This invention comprises plurality of edge illuminated photodiodes. More specifically, the photodiodes of the present invention comprise novel structures designed to minimize reductions in responsivity due to edge surface recombination and improve quantum efficiency. The novel structures include, but are not limited to, angled facets, textured surface regions, and appropriately doped edge regions.

FIELD OF THE INVENTION

The present invention is directed toward photodiodes having improved operational and structural characteristics. More specifically, the present invention is directed towards novel edge illuminated photodiodes, and applications using the same, possessing high responsivity, enhanced quantum efficiency using n+ diffused region, and p+ textured region on silicon, and InGaAs/InP substrates respectively.

BACKGROUND OF THE INVENTION

Photodiodes comprise a plurality of electrode radiation-sensitive junctions formed in semiconductor material. Within a photodiode, charge carriers are created by light that illuminates the junction and photo current is generated dependent upon the degree of illumination. Photodiodes are used for detection of optical power and subsequent conversion of the same to electrical power. Operationally, photodiodes absorb photons and charged particles, which facilitate detection of incident optical power, thereby generating current proportional to the incident power.

Photodiodes are typified by the quantification of certain characteristics, such as electrical, optical, current (I), voltage (V), and noise. Electrical characteristics predominantly include shunt resistance, series resistance, junction capacitance, rise or fall time and frequency response whereas optical characteristics include responsivity, quantum efficiency, non-uniformity, and non-linearity. Noise in photodiodes is generated by a plurality of sources including, but not limited to, thermal noise, quantum or photon or shot noise, and flicker noise.

In the semiconductor industry it is often desirable to increase light-induced current of photodiodes in order to increase the signal-to-noise ratio and thereby enhance photodiode sensitivity. Photodiode sensitivity is crucial in low light-level applications and is typically quantified by noise equivalent power (NEP) defined as the optical power that produces a signal-to-noise ratio of unity at the detector output. NEP is usually specified at a given wavelength and over a frequency bandwidth of 1 Hz and is therefore expressed in units of W/Hz^(1/2).

Silicon photodiodes, essentially active solid-state semiconductor devices, are among the most popular photodetectors providing high performance over a wide wavelength range. For example, silicon photodiodes are sensitive to light in the wide spectral range, approximately 200*10⁻⁹ m to 1200*10⁻⁹ m, extending from deep ultraviolet all the way through visible to near infrared. Additionally, silicon photodiodes detect the presence or absence of minute light intensities thereby facilitating precise measurement of the same on appropriate calibration. For instance, appropriately calibrated silicon photodiodes detect and measure light intensities varying over a wide range, from very minute light intensities of below 10⁻¹³ watts/cm² to high intensities above 10⁻³ watts/cm².

Silicon photodiodes can be employed in an assortment of applications including, but not limited to, spectroscopy, distance and speed measurement, laser ranging, laser guided missiles, laser alignment and control systems, optical free air communication, optical radar, radiation detection, optical position encoding, film processing, flame monitoring, scintillator read out, environmental applications such as spectral monitoring of earth ozone layer and pollution monitoring, low light-level imaging, such as night photography, nuclear medical imaging, photon medical imaging, and multi-slice computer tomography (CT) imaging, security screening and threat detection, thin photochip applications, and a wide range of computing applications.

Several problems exist with conventional photodiodes currently in use. In particular, for relatively short wavelength illumination, for instance below 800 nm, edge-illuminated silicon photodiodes absorb light very strongly near the edge surfaces thereby leading to low responsivity due to edge surface recombination. Likewise, controlling quantum efficiency, specifically in case of edge illuminated InGaAs/InP photodiodes, still remains a challenge.

The prior art fails to describe edge illuminated photodiodes that provide for lesser susceptibility to surface recombination effects, and possess high responsivity, and high quantum efficiency respectively. Consequently, there is still a need for photodiodes possessing high responsivity and high quantum efficiency. More specifically, there is demand for high responsivity edge illuminated silicon photodiodes having lesser susceptibility to surface recombination effects, which in turn is accountable for minimization of responsivity. Furthermore, high quantum efficiency edge illuminated InGaAs/InP photodiodes are also still needed.

SUMMARY OF THE INVENTION

The present invention is directed toward photodiodes having improved operational and structural characteristics. In one embodiment, the present invention is a photodiode comprising a substrate with at least a plurality of facets, wherein said plurality of facets comprise a proximate facet substantially comprising a region doped with an impurity of a first conductivity type; a distant facet parallel to the proximate facet; a top facet having an anode metallization region and having a region proximate to said anode metallization region doped with an impurity of a second conductivity type; a bottom facet having a cathode metallization layer; a left facet; and a right facet parallel to the left facet.

In a second embodiment, the present invention is a photodiode comprising a substrate with at least a plurality of facets, wherein said plurality facets comprise a proximate facet; a distant facet, having an inner face and an outer face, parallel to the proximate facet; a top facet having an anode metallization region and a textured region doped with an impurity of a selected conductivity type; a bottom facet, having an inner face and an outer face, parallel to the top facet and further comprising a cathode metallization layer; a left facet; a right facet parallel to the left facet; and an angled facet having an inner face and an outer face, wherein the inner face of said angled facet forms an angle with the inner face of said distant facet of greater than 90 degrees.

In another embodiment, the present invention is a photodiode comprising a substrate with at least a plurality of facets, wherein said plurality facets comprise a proximate facet; a distant facet, having an inner face and an outer face, parallel to the proximate facet; a top facet having a metallization region, a region doped with an impurity of a first conductivity type, and at least two regions doped with an impurity of a second conductivity type wherein said second conductivity type is different from said first conductivity type; a bottom facet, having an inner face and an outer face, parallel to the top facet and further comprising a metallization layer; a left facet; a right facet parallel to the left facet; and an angled facet having an inner face and an outer face, wherein the inner face of said angled facet forms an angle with the inner face of said distant facet of greater than 90 degrees.

In another embodiment, the present invention is a photodiode comprising a substrate having a first conductivity type, a top region, and a bottom region; a metallization layer of the first conductivity type extending the length of the bottom region; a V-groove extending the width of said top region; an oxide layer extending the full length of the top region; a metallization region of a second conductivity type extending above the top region and through said oxide layer; and a layer diffused with said second conductivity type positioned below said oxide layer in the top region and extending the length of said V-groove, wherein said layer is in physical communication with said metallization region of the second conductivity type. Optionally, the photodiode has a layer of film covers the top region and wherein said layer creates a substantially planar surface above the V-groove.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other features and advantages of the present invention will be appreciated, as they become better understood by reference to the following detailed description when considered in connection with the accompanying drawings:

FIG. 1 a is a perspective view of one embodiment of an edge illuminated photodiode;

FIG. 2 a is a perspective view of another embodiment of the edge illuminated photodiode of the present invention;

FIG. 2 b depicts a flipped perspective view of the edge illuminated photodiode of FIG. 2 a;

FIG. 2 c, is a perspective view of another embodiment of an edge illuminated photodiode of the present invention;

FIG. 2 d depicts two distinct stages, prior to and subsequent to photochip dicing, using two schematic diagrams;

FIG. 3 a is a perspective view of another embodiment of the present invention, comprising PN-junctions on both the front and back surfaces;

FIG. 3 b is a schematic view of another embodiment of the present invention, comprising PN-junctions on both the front and back surfaces;

FIG. 3 c is a schematic view depicting PN-junctions and the depletion region of another embodiment of the present invention;

FIG. 4 a is a schematic view of another embodiment of the present invention, comprising an interior V-groove;

FIG. 4 b is a schematic view of another embodiment of the present invention, comprising an interior V-groove and a layer of film; and

FIG. 5 is a schematic view of another embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

The invention described herein comprises a plurality of photodiodes, optionally constructed as a diode array, each comprising n+ diffused regions, or angled facets and textured p+ regions. These photodiodes have improved performance characteristics, including, but not limited to, improved responsivity and enhanced quantum efficiency.

The photodiodes of the present invention can be constructed using semiconductor materials known to persons of ordinary skill in the art. In one embodiment, edge illuminated photodiodes are formed on photochips of semiconductor materials, including, but not limited to, Indium Gallium Arsenide (InGaAs), Indium Phosphide (InP), or silicon respectively. These photochips may be cuboidal in geometry possessing at least a plurality of sides, also referred to as a face or facet.

In a first embodiment, the edge illuminated photodiode is incorporated in a photochip having six distinct facets, namely proximate, distant, top, bottom, left, and right respectively. The proximate and distant facets are substantially parallel to each other. The top and bottom facets are substantially parallel to each other, and the left and right facets are substantially parallel to each other. The proximate facet substantially comprises an n+ diffused region. The bottom facet comprises a cathode metallization layer. The top facet comprises two regions, namely an anode metallization region and a p+ doped region. The p+ doped region is juxtaposed to the anode metallization region.

In second embodiment, an edge illuminated photodiode is incorporated in a substrate having seven distinct facets. Six facets include a proximate, distant, top, bottom, left, and right facet, respectively. The proximate and distant facets are substantially parallel to each other. The top and bottom facets are substantially parallel to each other, and the left and right facets are substantially parallel to each other. The seventh facet is formed at an angle to no less than two facets, i.e., the distant and bottom facets, respectively. Preferably the angle of formation, measured relative to the internal face of each facet (the sides facing the inside of the photodiode), is greater than 90 degrees. More preferably, the angle of formation is 135 degrees.

In one embodiment, the top facet comprises two regions, namely an anode metallization region and a p+ doped and textured region. The p+ region, juxtaposed to the anode metallization region, is textured to reduce reflectance at this surface, thereby improving quantum efficiency of the photodiode. The p+ region is preferably textured to form a plurality of square base pyramids therein. Alternatively, the top facet comprises three regions: a p+ doped region and two n+ doped regions where the peripheral portion of both the n+ doped regions is delimited by a metallic plate. The bottom facet is comprises a cathode metallization layer.

The present invention is directed towards detector structures for an assortment of applications. More specifically, the present invention is directed towards novel edge illuminated photodiodes, and applications using the same, possessing high responsivity and enhanced quantum efficiency using n+ diffused region and p+ textured region for P on N silicon or p+ diffused region and n+ textured region for N on P silicon and InGaAs/InP substrates. Various modifications to the preferred embodiment will be readily apparent to those of ordinary skill in the art, and the disclosure set forth herein may be applicable to other embodiments and applications without departing from the spirit and scope of the present invention and the claims hereto appended. Thus, the present invention is not intended to be limited to the embodiments described, but is to be accorded the broadest scope consistent with the disclosure set forth herein.

The present invention comprises several embodiments that provide for lesser susceptibility to surface recombination effects and reflectance and absorption losses and further provides for enhanced responsivity and improved quantum efficiency. In one embodiment, the present invention comprises an edge illuminated photodiode that incorporates an n+ diffused region, which facilitates the minimization of edge surface recombination. Referring now to FIG. 1 a, photodiode 101 a is shown. Photodiode 101 a comprises photochip 100 a, which is made of a suitable semiconductor material possessing apt geometrical specifications. For example, and by no way of limitation, photochip 100 a comprises silicon that is cuboidal in geometry.

The cuboid (or rectangular parallelepiped) shaped photochip 100 a has six distinct facets. For purposes of elucidation, the sides or facets of photochip 100 a have been enumerated as proximate 102 a, distant 103 a, top 104 a, bottom 105 a, left 106 a, and right 107 a. Persons of ordinary skill would appreciate that the present designation of photochip geometry is not limited to the description provided herein and can be adjusted to suit other design, fabrication, and functional specifications.

A substantial portion of proximate facet 102 a comprises region 108 a possessing characteristics designed to improve responsivity and quantum efficiency. Region 108 a may be heavily doped, utilizing diffusion or implant techniques, with a suitable dopant of a particular conductivity type, such as p-type or n-type. In one preferred embodiment, an n-type dopant is used. Varieties of n-type dopants are known in this regard for instance, phosphorus (P), arsenic (As), antimony (Sb), among others. In one embodiment, the n+ doping layer is about 0.5 um to 1 um deep and can improve quantum efficiency by about 50% to about 80% depending on the wavelength, i.e. improving by 80% at 550 nm and by 50% at 850 nm.

A substantial portion of proximate facet 102 a may be subjected to controlled n+ diffusion to generate an n+ diffused region 108 a. There are many different approaches available in the prior art to carry out diffusion process, such as ion-implantation etc. However, the choice of the diffusion method is dependent on various factors, such as diffusion coefficient of the dopant, permissible error in diffusion depth, diffusion source, among other variables. It must be noted that the task stated above, such as diffusion, is routine undertaking of engineering for those of ordinary skill in the art having the benefit of this disclosure and, therefore, will not be further detailed herein.

The n+ diffused region 108 a assists in minimizing a reduction in responsivity of photodiode chip 101 a. Typically, a reduction in responsivity occurs due to edge surface recombination. The existence of n+ diffused region 108 a helps generate an electric field that facilitates the repulsion of minority carriers, thereby minimizing recombination. It is therefore preferred that, in the formation of n+ diffused region 108 a, dopant concentration should significantly exceed photogenerated carrier concentration. It must be noted that a heavily doped region juxtaposed to a relatively lightly doped region forms a high low n+ n junction, which acts as a low recombination velocity surface thereby facilitating minimization or reduction of surface recombination. Likewise, n+ diffused region 108 a juxtaposed to a relatively lightly doped bulk region, specifically portion of photochip 100 a flanking n+ diffused region 108 a, forms an interface that acts as a low recombination velocity surface, thereby minimizing surface recombination.

Top facet 104 a comprises two regions, 113 a and 111 a. Region 113 a is essentially a heavily doped region. Region 113 a may be doped with an appropriate impurity or dopant of selected conductivity type, such p-type or n-type. For instance, and by no way of limitation, a p-type dopant, such as boron, is preferred.

Region 111 a comprises an anode metallization region. Appropriate metal is utilized in the formation of anode metallization region. For instance, use of gold (Au) or aluminum (Al) is preferred. Metallization can be accomplished using any of a number of known approaches, including, for instance, subtractive processes, fully additive processes, and semi-additive processes. Metallization is performed using an assortment of techniques including, but not restricted to, evaporation, sputtering, plating, or electrolytic or electroless. More specifically, semiconductor devices employ metallization primarily to serve at least dual purpose: a) to form an electrical contact and b) to form an interconnection means within die circuits. Known processes make use of appropriate metals and/or alloys as materials for metallization. For instance, thin-film aluminum is most extensively exploited material for metallization and, due to low resistivity and adhesion compatibility with silicon dioxide, is very suitable for metallization. A disadvantage of aluminum as metallization material is low melting temperature, i.e. 660° C., and low Al—Si eutectic temperature, i.e. 577° C. These restrict the maximum processing temperature once the aluminum layer has been deposited.

In one embodiment, bottom facet 105 a is subjected to metallization. Accordingly, bottom facet 105 a includes a cathode metallization layer 109 a, which preferably comprises, but is not limited to, gold (Au).

In a second embodiment, the present invention comprises an edge illuminated photodiode incorporated in a suitable semiconductor substrate with an angled facet and a textured p+ surface. The textured p+ surface reduces reflectance thereby enhancing the quantum efficiency of the photodiode.

Referring now to FIG. 2 a, an embodiment of an edge illuminated photodiode of the present invention is shown. Photodiode 201 a comprises photochip 200 a, which is made of a suitable semiconductor material possessing apt geometrical specifications. For example, and by no way of limitation, photochip 200 a comprises silicon that is cuboidal in geometry. The cuboid (or rectangular parallelepiped) shaped photochip 200 a has six distinct facets. For purposes of elucidation, the sides or facets of photochip 200 a have been enumerated as proximate 202 a, distant 203 a, top 204 a, bottom 205 a, left 206 a, and right 207 a. Persons of ordinary skill would appreciate that the present designation of photochip geometry is not limited to the description provided herein and can be adjusted to suit other design, fabrication, and functional specifications.

Bottom surface 205 a is subjected to metallization in accord with the principles of the present invention. Consequently, bottom facet 205 a comprises a cathode metallization layer 208 a. For example, and by no way of limitation, the use of gold (Au) is preferred.

Top facet 204 a comprises two regions, 211 a and 213 a. Region 213 a is essentially a heavily doped region. Region 213 a may be doped with an appropriate impurity or dopant of selected conductivity type, such p-type or n-type. For instance, and by no way of limitation, a p-type dopant, such as Zn in InP/InGaAs photodiodes and boron in silicon photodiodes, is preferred. Region 211 a comprises an anode metallization region. Appropriate metal is utilized in the formation of anode metallization region. For instance, use of gold (Au) or aluminum (Al) is preferred.

In one embodiment, the amount of light absorbed by the semiconductor substrate is improved by modifying the photodiode surface. Two mechanisms are primarily accountable for the minimization or reduction of the amount of light absorbed by a photodiode. First, light may be reflected off the semiconductor substrate, i.e. reflection losses. Second, light may enter the substrate and exit without having been absorbed, i.e. absorption losses. Both of these loss mechanisms can be controlled by the modifying the photodiode surface in an attempt to attain surface imperfections. Surface imperfections can be achieved via roughening or texturing of the substrate surface.

Surface texture plays a vital role in facilitating confinement or trapping of light within the photochip. Texture includes roughness, waviness, and lay, namely short wavelength deviations of a surface from the nominal surface. Surface texturization, or surface texturing, is responsible for altering the transmission properties of semiconductor surfaces within devices. Surface texturing facilitates 1) confinement or trapping of light, and 2) reduces reflectance thereby improving the quantum efficiency of devices. For instance, reflection losses are diminished via increment in the probability that a light ray will strike the substrate surface multiple times, whereas absorption losses are reduced via light confinement within the substrate body, called light trapping. Surface texturization of material is known to persons of ordinary skill in the art. In general, surface texturization is executed either via isotropic (dissolution) or anisotropic etching.

Surface textured region 210 a is shown in FIG. 2 a and is further detailed in FIG. 2 b. FIG. 2 b depicts a flipped perspective view of the edge illuminated InGaAs/InP photodiode 201 a of FIG. 2 a. In one embodiment, region 210 b may be textured utilizing apt surface texturing techniques, irrespective of the crystallographic orientation of InGaAs/InP crystal, in an attempt to cause surface modifications thereupon through the formation of a plurality of convexities and concavities. These convexities and concavities possess apposite geometrical and dimensional specifications. For example, region 210 b may be textured preferably forming a plurality of three-dimensional (3-D) square base pyramidal prisms therein. It must be noted here that the square base pyramidal prisms facilitate light trapping or confinement within photodiode 201 b. In this regard, several texturing techniques are known that do not rely on crystallographic orientation, including reactive ion etching.

Referring back to FIG. 2 a, a seventh facet 214 a is positioned between two facets, preferably 203 a and 205 a. The seventh facet 214 a is angled relative to distant facet 203 a and bottom facet 205 a. The angle of formation between the inner face of the seventh facet 214 a and the inner face of distant facet 203 a is between 90 and 180 degrees, preferably around 135 degrees. The angle of formation between the inner face of the seventh facet 214 a and the inner face of bottom facet 205 a is between 90 and 180 degrees, preferably around 135 degrees.

Angled facet 214 a may be fabricated utilizing appropriate etching techniques. Typically, angled facets may be fabricated in an assortment of ways including, but not restricted to, wet etching and dry etching. A person of ordinary skill in the art would know how to fabricate angled facet 214 a.

In one embodiment, photodiode 201 a possesses the following specifications: device type is InP/InGaAs PIN photodiode; detection range varies from a minimum of approximately 800 nm to a maximum of approximately 1700 nm (i.e. optical bandwidth); active area diameter is typically 85 μm; operating voltage is typically −5 V; responsivity is at a minimum of approximately 0.70 A/W; dark current is <1 nA; reverse breakdown voltage is a minimum of 20 V; bandwidth is approximately 1 GHz; capacitance is 1 pF (when measured @Vr=−5 V); operating temperature varies from a minimum of −40° C. to a maximum of 85° C.; chip size is 350*350 μm typical; chip thickness is 200 μm typical; and detectable area 75*35 μm. All parameters, discussed above, are applicable for a chip temperature range of −40° C. to +85° C. and include any detrimental effects due to end of life (EOL) characteristics. The above specifications are merely for the purposes of elucidation, and are not limiting. Various modifications to the disclosed embodiments will be readily apparent to those of ordinary skill in the art, and the disclosure set forth herein may be applicable to other embodiments and applications without departing from the spirit and scope of the present invention and the claims hereto appended.

A third embodiment of an edge illuminated photodiode of the present invention is depicted in FIG. 2 c. Photodiode 201 c comprises photochip 200 c, which is made of a suitable semiconductor material possessing apt geometrical specifications. For example, and by no way of limitation, photochip 200 c comprises silicon that is cuboidal in geometry. The cuboid (or rectangular parallelepiped) shaped photochip 200 c has six distinct facets. For purposes of elucidation, the sides or facets of photochip 200 c have been enumerated as proximate 202 c, distant 203 c, top 204 c, bottom 205 c, left 206 c, and right 207 c. Persons of ordinary skill would appreciate that the present designation of photochip geometry is not limited to the description provided herein and can be adjusted to suit other design, fabrication, and functional specifications.

Bottom surface 205 a is subjected to metallization in accordance with the principles of the present invention. Consequently, bottom facet 205 a comprises a finish layer 220 c. For example, and by no way of limitation, the use of gold (Au) is preferred.

Top facet 204 c comprises at least four regions, enumerated herein as first 208 c, second 209 c, third 210 c, and fourth 211 c. First region 208 c is heavily doped, utilizing suitable diffusion techniques, with an apt impurity of the selected conductivity type, such as p-type or n-type. For instance, region 208 c is p+ doped. Region 208 c may be doped with a p-type dopant selected the group including Zn or Be for InP material and boron or gallium for silicon. In one embodiment, first region 208 c possesses the following specifications: dimensions (length*breadth) of approximately 75 μm*35 μm and the breadth-wise distance of longer edge of first region 208 c from the distant edge of top facet 204 c is 70 μm.

In one embodiment, region 208 c is textured using surface texturing techniques to cause surface modifications thereupon. These convexities and concavities possess apposite three-dimensional (3-D) geometrical specifications. For instance, this region 208 c is textured to form a plurality of square base pyramidal prisms therein. It must be noted here that square base pyramidal prisms facilitate light trapping or confinement within the photochip 200 c.

Second region 209 c is preferably subjected to anode metal plating techniques. For example, and by no way of limitation, the use of gold (Au) as plating metal is preferred. Regions 210 c and 211 c are heavily doped with an impurity of a selected conductivity type, such as p-type or n-type. For example, regions 210 c and 211 c are preferably n+ doped. In one embodiment, a peripheral portion of regions 210 c and 211 c is delimited by a length of cathode metal plating. For example, and by no way of limitation, the use of gold (Au) as cathode plating metal is preferred.

Referring back to FIG. 2 c, a seventh facet 212 c is positioned between two facets, preferably 203 c and 205 c. The seventh facet 212 c is angled relative to distant facet 203 c and bottom facet 205 c. The angle of formation between the inner face of the seventh facet 212 c and the inner face of distant facet 203 c is between 90 and 180 degrees, preferably around 135 degrees. The angle of formation between the inner face of the seventh facet 212 c and the inner face of bottom facet 205 c is between 90 and 180 degrees, preferably around 135 degrees. Angled facet 212 c may be fabricated utilizing appropriate etching techniques.

Operationally, whenever a single mode fiber 250 c emanating light at wavelengths varying from a minimum of approximately 1300 nm to a maximum of approximately 1550 nm is positioned in vicinity of proximate facet 202 c, comprising a detectable area (i.e. 75 μm*35 μm), light penetrates through the photodiode chip 201 c, gets reflected by angled edge 214 c, bends by 90°, and is incident on the textured p+ region 208 c. P+ region is textured in an attempt to decrease reflectance at this surface thereby improving quantum efficiency of photodiode 201 c.

In current embodiment, the photodiode 201 c may preferably possess the following preliminary specifications: device type is InP/InGaAs PIN photodiode; detection range varies from a minimum of approximately 800 nm to a maximum of approximately 1700 nm (i.e. optical bandwidth); active area diameter of about 85 μm; operating voltage of about −5 V; responsivity at a minimum of approximately 0.70 A/W; dark current is <1 nA; reverse breakdown voltage is a minimum of 20 V; bandwidth is about 1 GHz; capacitance is about 1 pF (when measured @Vr=−5 V); operating temperature varies from a minimum of −40° C. to a maximum of 85° C.; chip size is 350*350 μm typical; chip thickness is 200 μm typical; and detectable area 75*35 μm. All parameters, discussed above, are applicable for a chip temperature range of −40° C. to +85° C. and include any detrimental effects due to end of life (EOL) characteristics.

Another embodiment of the edge illuminated photodiode of the present invention is depicted in FIG. 2 d which illustrates two distinct stages: prior to, and subsequent to, photochip dicing. Photochip 200 d, prior to dicing, comprises a photodiode 201 d having two primary regions, 202 d and 203 d. First region 202 d comprises alternating heavily doped regions, such as 214 d and 216 d, doped with impurities of selected conductivity types. For example, but not limited to such example, first heavily doped region 214 d is doped with a suitable impurity of a first selected conductivity, i.e. n-type, whereas second heavily doped region 216 d is doped with a suitable impurity of a second selected conductivity type, in opposition to first, i.e. p-type. These alternating heavily doped regions are positioned proximate to the front side of device photochip 200 d.

In one embodiment, second region 204 d is in essence a passivation layer selectively grown atop front side of photochip 200 d. For example, use of materials including, but not limited to, silicon nitride, silicon oxide, silicon oxynitride or a layered combination of the aforementioned materials, etc. is preferred for the formation of the passivation layer. Regions 224 d and 226 d, which are devoid of the passivation layer and positioned immediately atop heavily doped regions, 214 d and 216 d respectively, are preferably subjected to selective metallization.

The photodiode chip after photochip dicing is manufactured by eliminating region 218 d, shown in the photodiode chip before photochip dicing. To eliminate region 218 d, an initial v-groove 205 d is manufactured in the photochip 200 d. Typically, the photochip 200 d is first coated with a layer of first masking material on its back side. Preferably, the first masking layer may be fabricated from materials, such as those of silicon dioxide (i.e. SiO.sub.2), or silicon nitride (i.e. Si.sub.3 N.sub.4). Although use only of certain masking materials, such as those of silicon dioxide or silicon nitride, has been recommended persons of ordinary skill would appreciate that the utilization of materials for the fabrication of the first masking layer is not limited to the aforesaid materials and can be changed to suit other requirements.

Once the first masking layer is applied to the back side of the photochip, it is then superimposed with another conventional photoresist mask, thereby forming a second masking layer over the photochip. Using any of conventional photolithographic techniques including, but not restricted to, optical, UV (i.e. ultraviolet), EUV (i.e. enhanced ultraviolet) photolithography, e-beam or ion-beam lithography, x-ray lithography, interference lithography, etc. a pattern is rendered on the photoresist mask or layer. The photoresist is exposed and developed, thereby exposing the photochip through the pattern. For instance, and by no way of limitation, use is made of a buffered hydrofluoric acid (i.e. H.F.sub.3) to etch the first masking layer preferably made of SiO.sub.2. As an alternative, dry plasma gas etching can be used.

After the photoresist is locally removed and the first masking layers are etched, the photoresist is stripped off from the photochip and the photochip subjected to anisotropic etching with, for example, a mixture of HBR:H₂0₂:H₂0=1:1:3 can be used to create the V-groove in the InP layer. Typically, the finished width of V-grooves can be controlled to within 0.5 to 1 μm, such control being achieved using silicon nitride masks and EDP as the etchant.

The first masking layer is then stripped off the photochip. Portions of the photochip through the pattern in the first masking layer are typically, anisotropically etched to create the desired features (i.e., the v-groove) that lie in the back side of photochip vicinal crystal plane. For example, and not intended to be limiting, use is made of anisotropic etching technique to form the three dimensional v-groove on the back side of the photochip 200 d at suitable position, such as 205 d, as shown in FIG. 2 d. It must be noted here that inner wall of V-groove 205 d is coated with an appropriate anti-reflective (AR) layer. For example, use of silicon nitride as AR layer is preferred. After dicing the photochip into dies, the region 218 d is automatically removed.

Referring to FIG. 3A, in another embodiment, the present invention is directed toward a photodiode 300 a having a top surface 315 a and a bottom surface 345 a separated by p-type silicon 335 a. Located proximate to the top surface 315 a and bottom surface 345 a are p+ regions 320 a and n+ regions 325 a. An anode metal layer 305 a is plated atop the p+ 320 a regions and a cathode metal layer 310 a is plated atop the n+ regions 325 a. During operation, as also shown in FIG. 3C, depletion regions 330 a, 330 c form around the n+ regions 325 a, 325 c proximate to both the top 315 a and bottom surfaces 345 a, and between p+ region 320 a, 320 c. It is advantageous to have PN-junctions on both the top and bottom surfaces for silicon side illuminated photodiodes operated in relatively low reverse bias mode. While a p-type silicon region 335 a is depicted having n+ depletion regions, it should be appreciated that the region types can be reversed, thereby having a n+ type silicon region 335 a with p+ depletion regions.

Referring to FIG. 3B, in another schematic view of the embodiment in FIG. 3A, a photodiode 300 b having a top surface 315 b and a bottom surface 345 b separated by p-type silicon 335 b is shown. Located proximate to the top 315 b and bottom 345 b surfaces are p+ 320 b and n+ 325 b regions. An anode metal layer 305 b is plated atop the p+ 320 b regions and a cathode metal layer 310 b is plated atop the n+ regions 325 b. During operation, depletion regions 330 b form around the n+ regions 325 b proximate to both the top 315 b and bottom 345 b surfaces. When a reverse bias is applied to both the top and bottom NP-junctions, the depletion regions extend quickly into the vertical direction and eventually merge together at a certain bias. The photogenerated carriers are collected immediately by the electric field of the extended depletion regions. Thus, the quantum efficiency, the speed of response, and the crosstalk are improved significantly.

In one embodiment, the distance between the centers of adjacent n+ regions 325 b is approximately 170 μm, and the distance between the centers of adjacent cathode metal layers 310 b is approximately 170 μm. In another embodiment, the distance between the edges of adjacent n+ regions 325 b is approximately 50 μm. In yet another embodiment, the width of an n+ region 325 b is approximately 120 μm.

In another embodiment, the present invention comprises an edge illuminated photodiode incorporated in a suitable semiconductor substrate with an interior placed V-groove. The interior placed V-groove reduces reflectance thereby enhancing the quantum efficiency of the photodiode.

Referring now to FIG. 4 a, photodiode 401 a is shown. Photodiode 401 a comprises photochip 400 a, which is made of a suitable semiconductor material possessing apt geometrical specifications. For example, and by no way of limitation, photochip 400 a comprises silicon that is cuboidal in geometry. In one embodiment the photochip 400A comprises n-type silicon.

Photodiode 401A comprises a top region 415A having an oxide layer 425A and a V-groove 418A penetrating the width of the top region 415A. Photodiode 401A further comprises a bottom region 445A having a n+ metallization layer 435A. Impinging within, and through, the oxide layer 425A is at least one p+ metallization region 455A.

Immediately below the oxide layer 425A in the top region 415A are two regions. The first region is a p+ diffused layer 408 a that extends for a portion of the length of the oxide layer 425A. The p+ layer 408A assists in minimizing a reduction in responsivity of photodiode chip 401A to incoming radiation 475A. The p+ layer does not extend the length of oxide layer 425A but does however, extend below the V-groove 418A in conjunction with the oxide layer 425A. The p+ layer is in physical communication with the p+ metallization region 455A. The second region is n-type silicon 409A.

Referring to FIG. 4B, the same photodiode of FIG. 4A is shown with the addition of a layer of film 428B, such as clear polymide film or undoped silica film. Photodiode 401B comprises a top region 415B having an oxide layer 425B and a V-groove 418B penetrating the width of the top region 415B. The addition of the layer of film 428B creates a substantially planar region above the V-groove and serves to make the photodiode 401B more rugged. Photodiode 401B further comprises a bottom region 445B having a n+ metallization layer 435B on top of a n+ diffused layer. Impinging within, and through, the oxide layer 425B is at least one p+ metallization region 455B.

Immediately below the oxide layer 425B in the top region 415B are two regions. The first region is a p+ diffused layer 408B that extends for a portion of the length of the oxide layer 425B. The p+ layer 408B assists in minimizing a reduction in responsivity of photodiode chip 401B to incoming radiation 475B. The p+ layer does not extend the length of oxide layer 425B but does however, extend below the V-groove 418B in conjunction with the oxide layer 425B. The p+ layer is in physical communication with the p+ metallization region 455B. The second region is n-type silicon 409B.

It should be appreciated that, since the p+ layer is created underneath the V-groove, the depletion region of the PN-junction exists deep below the front surface of the photodiode chip; therefore, photo-generated carriers from a side illumination will collect before they have a chance to recombine. Conversely, in a conventional photodiode 500 having a n+ bottom layer 545, n+ metal layer 535, a p+ layer 518, an anti-reflective layer 528, a depletion region 508, a p+ metal contact 555, an oxide layer 525, on n-type silicon 509, as shown in FIG. 5, photo-generated carriers 505, generated from a side illumination 575, have to travel a much longer distance to the depletion region and, therefore, are susceptible to carrier recombination loss.

It should be appreciated that the V-groove device of the present invention can be made more economically and efficiently than the embodiment depicted in FIG. 1 because the manufacturing process employs a wet KOH etch which is faster than the RIE etches required to manufacture the embodiment of FIG. 1. It should also be appreciated that the selected conductivity type of the aforementioned regions could be reversed, i.e. the n-type silicon photochip could be p-type, the n+ metallization layer could be p+, the p+ metallization region could be n+, and the p+ diffused layer in the top region could be n+, and still fall within the scope of the present invention. It should also be appreciated that the exemplary dimensions and doping characteristics are not limiting.

The photodiodes of the present invention can be employed in an assortment of applications including, but not limited to, spectroscopy, distance and speed measurement, laser ranging, laser guided missiles, laser alignment and control systems, optical free air communication, optical radar, radiation detection, optical position encoding, film processing, flame monitoring, scintillator read out, environmental applications such as spectral monitoring of earth ozone layer and pollution monitoring, low light-level imaging, such as night photography, nuclear medical imaging, photon medical imaging, and multi-slice computer tomography (CT) imaging, security screening and threat detection, thin photochip applications, and a wide range of computing applications.

The above discussion is aimed towards providing a preferred embodiment incorporating the novel aspects of the present invention and it should be understood that the foregoing illustration is not the only application where the present invention can be reduced down to practice. The present invention can be suitably modified to incorporate other possible embodiments as well. The scope of the invention is defined solely by the accompanying claims and within the scope of the claims; the present invention can be employed in various other situations. For example, circumstances wherein design and fabrication of edge illuminated photodiodes possessing an assortment of figures of merit, quantitative or numerical measure of performance characteristics, for instance, and by no way of limitation, low cost, economically, technically, and operationally feasible, high responsivity, high quantum efficiency using n+ diffused layer, p+ textured surface, and reliance on diverse photochips, such as InGaAs/InP, silicon, etc. is desired while still staying within the scope of the present invention. 

1. A photodiode comprising: a substrate with at least a plurality of sides, wherein said plurality of sides comprise: a first side substantially comprising a region doped with an impurity of a first conductivity type; a second side parallel to the first side; a top side having an anode metallization region and having a region proximate to said anode metallization region doped with an impurity of a second conductivity type; and a bottom side having a cathode metallization layer.
 2. The photodiode of claim 1 wherein the first conductivity type is p-type.
 3. The photodiode of claim 1 wherein the first conductivity type is n-type.
 4. The photodiode of claim 3 wherein the n-type conductivity is achieved using a n-type dopant.
 5. The photodiode of claim 4 wherein the n-type dopant is at least one of phosphorus, arsenic, or antimony.
 6. The photodiode of claim 4 wherein the n-type dopant creates a n+ doping layer and wherein said n+ doping layer I approximately 0.5 μm to 1 μm deep.
 7. The photodiode of claim 1 wherein the impurity of a second conductivity type is a p-type dopant.
 8. The photodiode of claim 7 wherein the p-type dopant is at least one of boron or InP/InGaAs.
 9. The photodiode of claim 1 wherein the cathode metallization layer of the bottom side comprises gold.
 10. A photodiode comprising: a substrate with at least a plurality of sides, wherein said plurality sides comprise: a first side; a second side, having an inner face and an outer face, parallel to the first side; a top side having an anode metallization region and a textured region doped with an impurity of a selected conductivity type; a bottom side, having an inner face and an outer face, parallel to the top side and further comprising a cathode metallization layer; and an angled side having an inner face and an outer face, wherein the inner face of said angled side forms an angle with the inner face of said second side of greater than 90 degrees.
 11. The photodiode of claim 10 wherein said photodiode has a detection range and wherein said detection range varies from 800 nm to 1700 nm.
 12. The photodiode of claim 10 wherein said photodiode has an active area diameter approximately 85 μm.
 13. The photodiode of claim 10 wherein said photodiode has an operating voltage of approximately −5 V.
 14. The photodiode of claim 10 wherein said photodiode has a minimum responsivity of approximately 0.70 A/W.
 15. The photodiode of claim 10 wherein said photodiode has a dark current of less than 1 nA.
 16. The photodiode of claim 10 wherein said photodiode has a minimum reverse breakdown voltage of 20 V.
 17. A photodiode comprising: a substrate with at least a plurality of sides, wherein said plurality sides comprise: a first side; a second side, having an inner face and an outer face, parallel to the first side; a top side having a metallization region, a region doped with an impurity of a first conductivity type, and at least two regions doped with an impurity of a second conductivity type wherein said second conductivity type is different from said first conductivity type; a bottom side, having an inner face and an outer face, parallel to the top side and further comprising a metallization layer; and an angled side having an inner face and an outer face, wherein the inner face of said angled side forms an angle with the inner face of said distant side of greater than 90 degrees.
 18. A photodiode comprising: a substrate with at least a plurality of sides, wherein said plurality of sides comprise: a first side substantially comprising a region doped with an impurity of a first conductivity type; a second side parallel to the first side; a top side having an anode metallization region and having a region proximate to said anode metallization region doped with an impurity of a second conductivity type; and a bottom side having a cathode metallization layer, wherein at least one face of the first, second, top or bottom side is subjected to surface texturization. 